TOOL STEEL
Cr12 / 1.2080 / DIN 2080 / X210Cr12 / AISI D3 / SKD1

toolsteel.com/tool-steel/1-2080-d3-steel-cr12-x' target='_blank'>1.2080 Steel Mechanical Properties:

DIN 2080 Steel having properties of High Carbon 2% and High chromium 12 % tool steel with high wear resistance. Its supply condition is normally annealed to easy machining which recommended hardness is 57-58 HRC after making the dies & tools.

DIN 2080 Steel Chemical  Composition :

C Mn Si Cr P S
1.90-2.20 0.15-0.45 0.10-0.40 11.00-12.00 ≤0.030 ≤0.030

  • Introduction

  • Heat Treatment

  • Applications

  • Equivalent Grade

  • 1.2080X210Cr12)Introduction:

    High carbon and high chromium, ledeburitic 12 % Cr alloyed cold work tool steel, high compressive strength, fairly good dimensional stable during heat treatment, extremely resistant to wear against abrasive and adhesive, low distortion, deep hardenability, non-deforming, medium toughness and good edge-holding properites. Not suitable for nitriding and electrical discharge machining.Similar to AISI D3 ,Cr12.

  • 1.2080 Tool steel Heat Treatment
    Annealing:

    Anneal at 900°C and slow furnace cool. Hardness after annealing will be approx. 225 brinell.

    Hardening:

    Pre heat slowly to 750/800°C and thoroughly soak. Continue heating the 1.2080 component to the final hardening temperature of 950/1000°C and allow the 1.2080 component to be heated through. Cool in air or quench in oil.

    Tempering:

    Heat uniformly and thoroughly at the selected tempering temperature and hold for at least one hour per inch of total thickness. Double tempering should be carried out with intermediate cooling to room temperature.

  • DIN 2080 Tool Steel Application:

    DIN 2080 is used in cold Dies & tooling application that required the achievement of high degree of accuracy in hardening & tempering, such as dies drawing, forming cold rolls, powder metal tooling and blanking and trimming dies, blanking dies for paper and plastics, shear blades , cold die punches , Ejector pins etc.

  • toolsteel.com/tool-steel/1-2080-d3-steel-cr12-x' target='_blank'>1.2080 Steels Equivalent grade:

    AISI JIS EN ISO GOST GB
    D3 SKD1 X210Cr12 Х12 Cr12